T1 - Preparation and characterization of chemically vapor deposited ZrO2 coating on nickel and ceramic fiber substrates
AU - Borst, Mark A.
AU - Lee, Woo Y.
AU - Zhang, Ying
AU - Liaw, Peter K.
PY - 1997/6
Y1 - 1997/6
N2 - Monoclinic ZrO2 was deposited on several metallic and ceramic substrates by reacting ZrCl4, CO2, and H2 at temperatures of 800° to 1050°C. Ni substrates reacted significantly in the ZrO2 coating environment since the coating was porous and contained a considerable amount of Ni. In contrast, the coating deposited on SiC and aluminoborosilicate fibers was highly crystalline, faceted, and dense without any apparent interaction with the substrate materials.
AB - Monoclinic ZrO2 was deposited on several metallic and ceramic substrates by reacting ZrCl4, CO2, and H2 at temperatures of 800° to 1050°C. Ni substrates reacted significantly in the ZrO2 coating environment since the coating was porous and contained a considerable amount of Ni. In contrast, the coating deposited on SiC and aluminoborosilicate fibers was highly crystalline, faceted, and dense without any apparent interaction with the substrate materials.
UR - http://www.scopus.com/inward/record.url?scp=0031162624&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0031162624&partnerID=8YFLogxK
U2 - 10.1111/j.1151-2916.1997.tb03022.x
DO - 10.1111/j.1151-2916.1997.tb03022.x
M3 - Article
AN - SCOPUS:0031162624
SN - 0002-7820
VL - 80
SP - 1591
EP - 1594
JO - Journal of the American Ceramic Society
JF - Journal of the American Ceramic Society
IS - 6
ER -