T1 - Reduction in Step Height Variation and Correcting Contrast Inversion in Dynamic AFM of WS2 Monolayers
AU - Godin, Kyle
AU - Cupo, Christian
AU - Yang, Eui Hyeok
N1 - Publisher Copyright:
© 2017 The Author(s).
PY - 2017/12/1
Y1 - 2017/12/1
N2 - A model has been developed to account for and prevent the anomalies encountered in topographic images of transition metal dichalcogenide monolayers using dynamic atomic force microscopy (dAFM). The height of WS2 monolayers measured using dAFM appeared to be increased or decreased, resulting from the interactions between the tip and the surface. The hydrophilic SiO2 substrate appeared higher than the weakly hydrophilic WS2 when the tip amplitude was low or at a high set point (high force). Large amplitudes and low set points corrected the step height inversion, but did not recover the true step height. Removing water from the sample resulted in an order of magnitude reduced variation in step height, but the WS2 appeared inverted except at low amplitudes and high set points. Our model explains the varying step heights in dAFM of TMDs as a result of varying tip-sample interactions between the sample and substrate, in the presence or absence of capillaries. To eliminate contrast inversion, high amplitudes can be used to reduce the effect of capillary forces. However, when capillaries are not present, low amplitudes and high set points produce images with proper contrast due to tool operation in the repulsive regime on both materials.
AB - A model has been developed to account for and prevent the anomalies encountered in topographic images of transition metal dichalcogenide monolayers using dynamic atomic force microscopy (dAFM). The height of WS2 monolayers measured using dAFM appeared to be increased or decreased, resulting from the interactions between the tip and the surface. The hydrophilic SiO2 substrate appeared higher than the weakly hydrophilic WS2 when the tip amplitude was low or at a high set point (high force). Large amplitudes and low set points corrected the step height inversion, but did not recover the true step height. Removing water from the sample resulted in an order of magnitude reduced variation in step height, but the WS2 appeared inverted except at low amplitudes and high set points. Our model explains the varying step heights in dAFM of TMDs as a result of varying tip-sample interactions between the sample and substrate, in the presence or absence of capillaries. To eliminate contrast inversion, high amplitudes can be used to reduce the effect of capillary forces. However, when capillaries are not present, low amplitudes and high set points produce images with proper contrast due to tool operation in the repulsive regime on both materials.
UR - http://www.scopus.com/inward/record.url?scp=85038630571&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85038630571&partnerID=8YFLogxK
U2 - 10.1038/s41598-017-18077-4
DO - 10.1038/s41598-017-18077-4
M3 - Article
C2 - 29259238
AN - SCOPUS:85038630571
VL - 7
JO - Scientific Reports
JF - Scientific Reports
IS - 1
M1 - 17798
ER -