Reduction of sodium-accelerated oxidation of silicon nitride ceramics by aluminium implantation

Y. Cheong, H. Du, S. P. Withrow

Research output: Contribution to journalArticlepeer-review

5 Scopus citations

Abstract

Norton NBD 200 silicon nitride ceramics were implanted with sodium to a dose of 7.0 × 1015cm-2 at 72 keV (1 at% peak sodium content at 100 nm). The sodium-implanted samples were further implanted with aluminium to 7.3 × 1015cm-2 at 87 keV (1 at% peak aluminium content at 100 nm). The implanted and unimplanted samples were oxidized in 1 atm dry oxygen at 1100 and 1300°C for 2-6 h. Profilometry and scanning electron microscopy measurements indicated that sodium implantation led to up to a two-fold increase in the oxidation rate of silicon nitride. The sodium effect was effectively neutralized when aluminium was co-implanted. The opposite effects of sodium and aluminium on the oxidation resistance of silicon nitride can be attributed to their different roles in modifying the structure and properties of the oxide formed.

Original languageEnglish
Pages (from-to)2391-2396
Number of pages6
JournalJournal of Materials Science
Volume32
Issue number9
DOIs
StatePublished - 1997

Fingerprint

Dive into the research topics of 'Reduction of sodium-accelerated oxidation of silicon nitride ceramics by aluminium implantation'. Together they form a unique fingerprint.

Cite this